HDPE Geomembranes

Product Details:

Share Your Product:

Request To Call Back Send Inquiry

Product Description

We have established ourselves as a quality focused organization, engaged in manufacturing and supplying a quality range of HDPE Geomembranes. These are widely used in the containment and management of solids, liquids & gases. To comply with the set industrial norms, we use best quality HDPE materials, to manufacture the products. Our quality inspectors check the HDPE Geomembranes on strength and quality parameters to offer a flawless range to the clients.

Features:

Water proof finishing
Biological erosion resistance
Low coefficient of thermal expansion

Further Details:

We are one of the largest firms in industry, involved in manufacturing and exporting a comprehensive range of HDPE Geo Membranes. We use best grade raw materials and sophisticated technologies in fabrication of these membranes, which are procured from genuine and certified vendors of the industry. These membranes are broadly acknowledged for their resistivity to chemicals, low permeability and easy installation.

Features:

Easy to install
Water resistant
Durable

Specifications:-

Material: HDPE, LDPE, LLDPE, PVC.
Thickness: 0.25 - 2.5 mm
Width: Within 8 M
Color: Black or as required

Specification

Property	Test Method	Nominal Values
Thickness, mm	ASTM D 751/1593/5199	1.0	1.5	2.0	2.5	3.0
Density, g/cc	ASTM D 792/1505	0.94	0.94	0.94	0.94	0.94
Strength at Break, N/mm	ASTM D 6693, Type IV	34	52	69	86	103
Strength at Yield, N/mm	ASTM D 6693, Type IV	16	25	33	41	50
Elongation at Break, %	ASTM D 6693, Type IV	750	800	800	800	800
Elongation at Yield, %	ASTM D 6693, Type IV	15	15	15	15	15
Tear Resistance, N	ASTM D 1004	146	222	293	369	445
Puncture Resistance, N	FTMS 101, Method 2065	267	400	533	667	800
Carbon Black Content, %	ASTM D 1603	2-3	2-3	2-3	2-3	2-3
Carbon Black Dispersion	ASTM D 3015	A1/A2	A1/A2	A1/A2	A1/A2	A1/A2
Dimensional Stability, % (each direction)	ASTM D 1204, 100°C 1hr	±1	±1	±1	±1	±1
Environmental Stress Crack Resistance, hr	ASTM D 1693, Cond. B	>2000	>2000	>2000	>2000	>2000
Low Temperature Brittleness, °C	ASTM D 746, Cond. B	<-84	<-84	<-84	<-84	<-84
Oxidative Induction Time, minutes	ASTM D 3895, 200°C Pure O2, 1 atm	100	100	100	100	100
Ozone Resistance	ASTM D 1149, 7 days 100ppm	No Cracks	No Cracks	No Cracks	No Cracks	No Cracks
Water Absorption, % wt. change	ASTM D 570	<0.01	<0.01	<0.01	<0.01	<0.01
Moisture Vapour Transmission, g/m²	ASTM E 96	<0.001	<0.001	<0.001	<0.001	<0.001
Melt Flow Index, g/10 minutes	ASTM D 1238, Cond. 190/2.16	<=1.0	<=1.0	<=1.0	<=1.0	<=1.0